Single Color PVDF Coated AL Alloy Coil Common specifications: thickness 0.5-1.2mm, width: 800mm-1650mm
Πολλοί χρήστες του χρώμα χάλυβας προϊόντα είναι αντιμετωπίζουν τέτοια προβλήματα%3α
1. The color bebes old: If your color steel panel does not use high weather-resistant paint, the color of the paint will gradually fade after a long period of wind and sun exposure, especially for brighter colors.
2. Rust on the surface: the substrate of color steel plate is iron plate. We know that iron plate is extremely easy to rust. After a long time of oxidation, the rust on the surface will give you a very headache. Rust on the surface will cause the paint surface to peel off, further affecting the appearance. In the end, there is no choice but to remove rust and repaint, που θα αιτία δευτερογενής κατανάλωση και επηρεάζει παραγωγή και χρήση.
3. The salvage value of recycling is low. If it is planned to be deκατεδαφισμένο, the price of the used color steel plate is extremely low. Επειδή of the paint surface, its price is even lower than that of ordinary scrap iron.
| Αλουμίνιο φύλλο φυσικό ιδιότητες | ||||||||
| Βαθμολογώ | Tem. |
Πάχος/mm | Εφελκυσμός δοκιμή αποτελέσματα στο δωμάτιο θερμοκρασία | κάμψη ακτίνα | ||||
| Εφελκυσμός αντοχή (Rm/MPa) |
μη αναλογική επέκταση tensile δύναμη (Rp0.2/MPa) |
επιμήκυνση μετά θραύση (m% 2f ποσοστό ) | ||||||
| Α50 χιλιοστά | A | 90 μοίρες | 180 μοίρες | |||||
| 3003 | H14 | >0.20-0.50 | 145-195 | 125 | 2 | _ | 0.5t | 2.0t |
| >0.50-1.50 | 2 | 1.0t | 2.0t | |||||
| >1.50-3.00 | 3 | 1.0t | 2.0t | |||||
| >3.00-6.00 | 4 | 2.0t | 一 | |||||
| 3003 | H22 | >0.20-0.50 | 120-160 | 80 | 6 | _ | 0t | 1.0t |
| >0.50-1.50 | 7 | 0.5t | 1.0t | |||||
| >1.50-3.00 | 8 | 1.0t | 1.0t | |||||
| >3.00-6.00 | 9 | 1.0t | 一 | |||||
| H24 | >0.20-0.50 | 145-195 | 115 | 4 | _ | 0.5t | 1.5t | |
| >0.50-1.50 | 4 | 1.0t | 1.5t | |||||
| >1.50-3.00 | 5 | 1.0t | 1.5t | |||||
| >3.00-6.00 | 6 | 2.0t | 一 | |||||
| 3004 | H14 | >0.20-0.50 | 220-265 | 180 | 1 | _ | 0.5t | 2.5t |
| >0.50-1.50 | 2 | 1.0t | 2.5t | |||||
| >1.50-3.00 | 2 | 1.5t | 2.5t | |||||
| >3.00-6.00 | 3 | 2.0t | 一 | |||||
| H24 H34 |
>0.20-0.50 | 220-265 | 170 | 3 | _ | 0.5t | 2.0t | |
| >0.50-1.50 | 4 | 1.0t | 2.0t | |||||
| >1.50-3.00 | 4 | 1.5t | 2.0t | |||||
| H16 | >0.20-0.50 | 240-285 | 200 | 1 | _ | 1.0t | 3.5t | |
| >0.50-1.50 | 1 | 1.5t | 3.5t | |||||
| >1.50-3.00 | 2 | 2.5t | 一 | |||||
| H26 H36 |
>0.20-0.50 | 240-285 | 190 | 3 | _ | 1.0t | 3.0t | |
| >0.50-1.50 | 3 | 1.5t | 3.0t | |||||
| >1.50-3.00 | 3 | 1.5t | 一 | |||||
| 3104 | H26 | >0.20-0.50 | 245 | _ | 1 | 2.0t | 2.0t | |
| >0.50-0.80 | 2 | 2.0t | 2.0t | |||||
| >0.80-1.30 | 3 | 2.5t | 2.5t | |||||
| >1.30-3.00 | 4 | 2.5t | 2.5t | |||||
| H18 H38 |
>0.20-0.50 | 265 | _ | 1 | _ | _ | _ | |
| H28 | >0.20-0.50 | 265 | _ | 1 | _ | _ | _ | |
| H19 H29 H39 |
>0.20-0.50 | 275 | _ | 1 | _ | _ | _ | |
| F | >0.20-0.50 | _ | ||||||
Είναι αδύνατο να συνειδητοποιήσει a ποικιλία των σχημάτων. Η σκληρότητα του χρώμα χάλυβα είναι σχετικά υψηλό % 2c και αυτό μπορεί πάει ευθεία. Εάν είναι λυγισμένο ή σχεδιασμένο σε άλλα σχήματα % 2c it θα είναι δύσκολο να συνειδητοποιήσει % 2c και ακόμη αν είναι μόλις και μετά βίας συνειδητοποιημένο% 2c η αισθητική δεν θα είναι πολύ καλό .
Τώρα ας μας εισάγουμε PVDF επικαλυμμένο AL κράμα πηνίο % 2c a τέλειο υποκατάστατο χρώμα χάλυβα πλάκα% 2c που έχει πολλά πλεονεκτήματα as ακολουθεί
1. Light weight: the density of aluminum is 2.73KG/M³, only 1/3 of that of of steel;
2. Υψηλή αντοχή: υψηλή αντοχή μπορεί είναι επιτυγχάνεται μέσω σύνθεση διαμόρφωση%2γ επεξεργασία και θερμότητα επεξεργασία μέθοδοι%3β
3. Corrosion resistance: with self-rust prevention ability, the formation of oxide layer, can prevent metal oxidation corrosion, good acid and alkali resistance;
4. Diverse surface treatment, beautiful: anodizing, electrophoresis, chemical treatment, polishing, painting treatment;
5. Καλή πλαστικότητα και εύκολη επεξεργασία;
6. Καλός ηλεκτρικός αγωγιμότητα: μη μαγνήτιση και χαμηλός σπινθήρας ευαισθησία, can prevent electromagnetic interference and reduce the flammability in special environment;
7. Easy installation: a aluminum metal can be riveted, welded, glued and other ways to connect;
8. Single Color PVDF Coated AL Alloy Coil Environmental protection: 100 percent recyclable.
PVDF is fluorocarbon paint which is a high-performance two-component coating with excellent physical and chemical properties. Fluorocarbon paint has the advantage of weather resistance, self-cleaning, corrosion resistance, solvent resistance, color retention and gloss retention, etc. The paint film has various colors , including solid paint and metallic flash paint. The fluorocarbon paints we use are all high-quality paints higher από 70 τοις εκατό φθοράνθρακας.
| Βαθμολογώ | χημικό συστατικό（ ποσοστό ） | |||||||||||
| Σι | Φε | Cu | Μν | Mg | Cr | Zn | Τι | άλλος | .AI | |||
| καθένας | σύνολο | |||||||||||
| 3A21 | 0.6 | 0.7 | 0.2 | 1.0~1.6 | 0.05 | / | 0.1 | / | 0.15 | 0.05 | 0.1 | Ισορροπία |
| 3003 | 0.6 | 0.7 | 0.05 ~0.20 | 1.0~1.5 | / | / | 0.1 | / | / | 0.05 | 0.15 | |
| 3103 | 0.5 | 0.7 | 0.1 | 0.9~1.5 | 0.3 | 0.1 | 0.2 | Ti plus Zr: 0.10 | / | 0.05 | 0.15 | Ισορροπία |
| 3004 | 0.3 | 0.7 | 0.25 | 1.0~1.5 | 0.8~13 | / | 0.25 | / | / | 0.05 | 0.15 | Ισορροπία |
| 3005 | 0.6 | 0.7 | 0.3 | 1.0~1.5 | 0.20 ~0.6 | 0.1 | 0.25 | / | 0.1 | 0.05 | 0.15 | Ισορροπία |
| 3105 | 0.6 | 0.7 | 0.3 | 0.30 ~ 0.8 | 0.20 ~0.8 | 0.2 | 0.4 | / | 0.1 | 0.05 | 0.15 | Ισορροπία |
| PVDF Αλουμίνιο φύλλο | |
| Single Color PVDF Coated AL Alloy Coil Parameter | |
| Ζωγραφική επίστρωση | Επάνω:20μm Πίσω:5μm |
| Χρώμα | Σύμφωνα με προς πελάτη αίτημα |
| Γυαλάδα | Πρότυπο: 25 plus 1-5 |
| Εγκάρσια τομή πρόσφυση | Το χρώμα φιλμ κάνει όχι πτώση απενεργοποίηση |
| T-bend test | 1T- το paint film does not fall off |
| Αντίστροφη πρόσκρουση | 9J -το χρώμα φιλμ κάνει όχι πτώση απενεργοποίηση |
| MEK δοκιμή | Βουτανόνη MEK σκούπισμα πίσω και πίσω 100 φορές χωρίς ζημιά στο το χρώμα φιλμ |
| Θερμότητα και υγρασία αντίσταση | Τοποθετημένο στο το χωρίς συμπύκνωση υγρασία θερμότητα δοκιμή θάλαμος για 1000 ώρες, όχι φυσαλίδες, ρωγμές, ξεφλούδισμα off του το χρώμα φιλμ, όχι αλλαγή in χρώμα, γυαλάδα και σκληρότητα |
| Οξύ και αλκάλια αντίσταση | Εμποτισμένο in 5 percent hydrochloric acid for 24 hours, no obvious change in appearance Soaked in 5 percent sodium oxide for 24 hours, no obvious change in appearance |
| Ουδέτερο αλάτι ψεκασμός αντίσταση | Ουδέτερο αλάτι ψεκασμός δοκιμή για 1000 ώρες |
| UV λάμπα επιταχυνόμενη γήρανση δοκιμή | OUVA-340} UV lamp test box 2000 hours of light, no bubbles, cracks and other defects. |